Nylon flame retardants

PA12 Flame Retardant CR-M1205

CR-M1205 is a novel flame retardant developed for PA12. It can get UL94-V0 @0.8-1.6mm. What's more, it can increase the elongation at break. At the same time, The low density of PA12 has also been retained. The modified FR PA12 can be applied in low-altitude economic sectors and wearable devices.

1. Materials：

PA12：WanHua L2000
Flame retardant：Inovia CR-M1205

2. Processing condition：

Drying：90-100 ℃, 4h
Extrusion temperature：200-220 ℃
Injection temperature：220-230 ℃; mold temperature 70-80 ℃

3. Application data

Table 1. Flame retardant performance

CR-M1205	UL 94 rating
13%	V0@0.8mm~1.6mm

Table 2. Mechanical properties

	Method	Unit	PA12	+13%CR-M1205
Tensile strength	ISO 527	MPa	47	42
Elongation at break	ISO 527	%	258	285
Flexural strength	ISO 178	MPa	51.5	26.2
Flexural modulus	ISO 178	MPa	1364	670
Charpy notched impact strength	ISO 179	kJ/m²	7.8	5.6

Table 3. Other properties

	Method	Unit	PA12	+13%CR-M1205
Melt index (220℃ / 2.16kg)	ISO 1133	cm³/10min	14.4	70.3
HDT (1.8MPa)	ISO 75	℃	40	30
density	ISO 1183-1	g/cm³	1.01	1.05

* The data recommended in this document can be used as a reference for various purposes. There will also be some amendments along with new technical improvements. Therefore, when designing the product, the use environment and structure of the product should be fully considered, and whether the product has any problems should be judged by the design company itself.